Photo-Cross-Linked Hydrogels from Thermoresponsive PEGMEMA-PPGMA-EGDMA Copolymers Containing Multiple Methacrylate Groups: Mechanical Property, Swelling, Protein Release, and Cytotoxicity

Photo-cross-linked hydrogels from thermoresponsive polymers can be used as advanced injectable biomaterials via a combination of physical interaction (in situ thermal gelation) and covalent cross-links (in situ photopolymerization). This can lead to gets with significantly enhanced mechanical properties compared to non-photo-crosslinked thermoresponsive hydrogels. Moreover, the thermally phase-separated gels have attractive advantages over non-thermoresponsive gels because thermal gelation upon injection allows easy handling and holds the shape of the gels prior to photopolymerization. In this study, water-soluble thermoresponsive copolymers containing multiple methacrylate groups were synthesized via one-step deactivation enhanced atom transfer radical polymerization (ATRP) of poly(ethylene glycol) methyl ether methacrylate (PEGMEMA, M-n = 475), poly(propylene glycol) methacrylate (PPGMA, M-n = 375), and ethylene glycol dimethacrylate (EGDMA) and were used to form covalent cross-linked hydrogels by photopolymerization. The cross-linking density was found to have a significant influence on the mechanical and swelling properties of the photo-cross-linked gels. Release studies using lysozyme as a model protein demonstrated a sustained release profile that varied dependent on the copolymer composition, cross-linking density, and the temperature. Mouse C2C12 myoblast cells were cultured in the presence of the copolymers at concentrations up to 1 mg/mL. It was found that the majority of the cells remained viable, as assessed by Alamar Blue, lactate dehydrogenase (LDH), and Live/Dead cell viability/cytotoxicity assays. These studies demonstrate that thermoresponsive PEGMEMA-PPGMA-EGDMA copolymers offer potential as in situ photopolyimerizable materials for tissue engineering and drug delivery applications through a combination of facile synthesis, enhanced mechanical properties, tunable cross-linking density, low cytotoxicity, and accessible functionality for further structure modifications.