Basicity and Electrolyte Composition Dependent Stability of Ni-Fe-S and Ni-Mo Electrodes during Water Splitting

Non-noble metal electro-catalysts for water splitting are highly desired when we are moving towards a society where green electrons are becoming abundantly available, offering clear prospects to make our society more sustainable. In this work, Ni-Fe-S is reported as a high performing anode material for the water splitting reaction, operating at low overpotentials and showing high apparent stability. Furthermore, Ni-Mo electrodes are developed on metallic foam substrates and optimized in terms of their performance. The Ni-Fe-S material as anode, combined and integrated with Ni-Mo as cathode in a cell configuration, splits water at 10 mA cm-2 and a potential of 1.55 V. Similar to previous reports, we confirm that Mo leaches from Ni-Mo/Ni foam electrodes. Cycling tests and ICP-AES measurements show that the stability of Ni-Fe-S is apparent, and that in reality S is leaching from the material as was already suggested in literature. We expand on this knowledge and show that the leaching of S is dependent on both pH and the cation used during electrocatalysis. Furthermore, we find that applying an oxidative potential is in truth stabilizing towards S and that the alkalinity causes leaching. S was furthermore mobile and found to segregate towards the surface. Finally, using too low pH values (11 and lower) result in the passivating hydroxide metal layers being destroyed and the Ni-Fe-S dissolving completely.